Belzona 1161 Super UW-Metal 1kg Kit 2-Part Metal Repair Composite Epoxy Resin Wet Oil Surface Underwater Application Sealing Joint Flange Solvent Free Structural Adhesive Room Temperature Cure

Belzona 1161 Super UW-Metal 1kg one Set Kit Base A 0.8kg + Solidifier B 0.2kg = 1kg A 2-part composite material for metal repair and resurfacing based on a solvent-free, surface-tolerant epoxy resin reinforced with silicon steel alloy. This composite material is specifically designed for application to wet and oil contaminated surfaces, as well as for underwater applications. It is easy to mix and apply without the need of specialist tools and can be machined using conventional tools. Bonds strongly to wet, oily and manually prepared surfaces Multi-purpose durable repair composite Application and cure at room temperature and underwater - no hot work involved Excellent bonding to metals including stainless steel, carbon steel, aluminium, brass, copper and other rigid surfaces Fully machinable using conventional tools Excellent electrical insulation Solvent-free. Reduced health and safety risks. No shrinkage, expansion or distortion Outstanding corrosion protection Excellent chemical resistance against a wide range of chemicals Repair of oil and water leaks Sealing of joints and flanges Repair of cracks and holes on engine and pump casings, transformers, pipes, tanks etc. Resurface of pitted metal surfaces High strength structural adhesive for metal bonding Creation of irregular load bearing shims and reforming of bearing housings Application Temperature: 41°F/5°C to 104°F/40°C Working Life: At 68°F/20°C usable life of mixed material: 16 minutes. Cure Times table 0.25 inch (6 mm) thickness: Machining / light loading: 6 hrs at 5°C, 4 hrs at 10°C, 2 hrs at 20°C, 1 hr at 30°C, 0.5 hr at 40°C. Full mechanical / thermal loading: 4 days at 5°C, 2 days at 10°C, 1 day at 20°C, 16 hrs at 30°C, 12 hrs at 40°C.

• Belzona 1161 Super UW-Metal Kit. 1kg one Set. Base A 0.8kg + Solidifier B 0.2kg = 1kg. 2 Parts Components Metal Repair Composite Epoxy Resin with silicon steel alloy. Wet Oil Surface Underwater Application. Solvent Free Structural Adhesive. Room Temperature Cure
• Application Temperature: 41°F/5°C to 104°F/40°C. Color: Grey. Base Density: 2.80 g/cm³. Base Gel Strength (HF paddle): >150 g/cm. Solidifier Density: 1.40 g/cm³. Solidifier Gel Strength (QV paddle): 90 g/cm. Mixing Ratio by Weight (Base : Solidifier): 4:1; by Volume: 2:1. Slump Resistance: >0.5 in / >12.7 mm. VOC (ASTM D2369): 0.10% / 2.39 g/L. Volume Capacity 428 cm³ (26.1 in³)/kg.
• Excellent bonding to metals including stainless steel, carbon steel, aluminium, brass, copper & other rigid surfaces. Repair of oil and water leaks. Sealing of joints and flanges. Repair of cracks and holes on engine and pump casings, transformers, pipes, tanks, etc. Resurface of pitted metal surfaces. Creation of irregular load bearing shims and reforming of bearing housings.
• Bonds strongly to wet, oily and manually prepared surfaces. Underwater Application. Cure at room temperature - no hot work involved. Excellent electrical insulation characteristics. Solvent-free. Reduced health and safety risks. Outstanding corrosion protection. Excellent chemical resistance. No shrinkage, expansion or distortion. Fully machinable using conventional tools.
• Cure Times table 0.25 inch (6 mm) thickness. Machining and/or light loading: 6 hrs at 5°C, 4 hrs at 10°C, 2 hrs at 20°C, 1 hr at 30°C, 0.5 hr at 40°C. Full mechanical or thermal loading: 4 days at 5°C, 2 days at 10°C, 1 day at 20°C, 16 hrs at 30°C, 12 hrs at 40°C.